MC®907 (NYLON TYPE 6 – CAST UNFILLED)
Material Information
Nylon 6 belongs to the cast nylon family of materials. Cast nylons offer the widest array of sizes or custom shapes of any thermoplastic. Nylons are a frequently used material as replacements for bronze, brass, aluminum, steel, and other metals, especially in bearing or wear applications. Nylons offer excellent wear and impact resistance, have high tensile strength and high modulus of elasticity, and have a high heat distortion temperature. They also resist wear, abrasion, and vibration. Nylons can also withstand a variety of chemicals, alkalis, oxidizing agents, and dilute acids. However, nylons do absorb moisture, so they are not recommended for wet applications. Because of its high crystalinity, Nylon 6 has better heat deflection, better solvent resistance, better hygroscopic characteristics, and better dimensional stability than Nylon 6/6. Nylon 6 is available in rod, tube, and sheet.
MC®907 is an unmodified cast type 6 nylon. MC®907 along with MC®901 have the highest strength and hardness of the nylon 6 grades. The natural colored MC®907 is FDA, USDA, and 3A-Dairy compliant.
Application
- Food contact parts
Properties
- Highest strength and hardness of nylons
- FDA, USDA, and 3A-Dairy compliant (natural)
- Lightweight
- Absorbs moisture
- High wear and impact resistance
- High modulus of elasticity
- High heat distortion temperature
- Resists wear, abrasion, and vibration
- High chemical resistance
Physical |
Astm Test Method |
MC®907 and
|
| Density (lb/in^3) | D792 | 0.042 |
| Specific Gravity | D792 | 1.15 |
| Water Absorption @ 24 hours (%) | D570 | 0.3 |
| Water Saturation (%) | D570 | 7 |
Mechanical |
||
| Tensile Strength (PSI) | D638 | 12,000 |
| Tensile Modulus (PSI) | D638 | 400,000 |
| Tensile Elongation at Break (%) | D638 | 20 |
| Flexural Strength (PSI) | D790 | 16,000 |
| Flexural Modulus (PSI) | D790 | 500,000 |
| Compressive Strength (PSI) | D695 | 15,000 |
| Compressive Modulus (PSI) | D695 | 400,000 |
| Izod Impact (Notched), ft-lb/in | D256 | 0.4 |
| Rockwell Hardness | D785 | R115 |
Thermal |
||
| Coefficient of Thermal Expansion, 10^-5/°F |
D696 | 3.5 |
| Heat Deflection Temperature 264 psi, ºF | D648 | 200 |
| Melting Point, °F | D3418 | 420 |
| Continous Service Temp (Operating), °F | – | 200 |
| Thermal Conductivity, BTU-in/hr-ft² °F | C177 | – |
| Flammability Rating | UL94 | HB |
Electrical |
||
| Dielectric Strength, Short Term, (Volts/Mil) @ .125″ Thick |
D149 | 500 |
| Volume Resistivity (ohm-cm) @ 73 ºF, 50% RH |
D257 | >10^13 |
| Dielectric Constant at 60Hz | D150 | 3.7 |
| Dissipation Factor at 60 Hz | D150 | – |
NOTE:
The information contained herein are typical values intended for reference and comparison purposes only. They should NOT be used as a basis for design specifications or quality control. Contact us for manufacturers' complete material property datasheets. All values at 73°F (23°C) unless otherwise noted.